| ZrO₂+HfO₂ | >94% |
| SiO₂ | < 0.015% |
| Fe₂O₃ | < 0.002% |
| Na₂O | < 0.005% |
| TiO₂ | <0.002% |
| Y₂O₃ | 5.56% |
| D50 | 64.67 μm |
| 主要成分 | Composition | W t% | ZrO₂+Y₂O₃≥99.5% |
| 密度 | Specific Density | g/cm3 | >6.05 |
| 硬度 | Hardness(HV) | Gpa | >12.0 |
| 热膨胀系数 | Coefficient of thermal expansion | (10-6/K) | 9.6(20-400°C) |
| 抗弯强度 | Bending Strength | Mpa | >1150 |
| 弹性模量 | Elastic Modulus | Gpa | 205 |
| 晶粒大小 | Grain Size | μm | <0.5 |
| 热导率 | Thermal Conductivity | W/(m-k) | 2.5 |
| 断裂韧性 | Fracture Toughness | Mpa m1/2 | 7-10 |
| 产品型号 | OZ-3Y | OZ-3YG | OZ-3YB | OZ-3YBG | OZ-3YW | OZ-4Y | OZ-8Y |
| Zr(Hf)O2(wt%)≥ | 94 | 94 | 89.5 | 89.5 | 94 | 92 | 86 |
| Y2O3(wt%) | 5.25±0.25 | 5.25±0.25 | 4.95±0.25 | 4.95±0.25 | 5.25±0.25 | 7.2±0.25 | 13.5±0.25 |
| Al2O3(wt%) | 0.23±0.02 | 0.23±0.02 | 0.23±0.02 | 0.23±0.02 | —— | —— | —— |
| SiO2(wt%)≤ | 0.0200 | 0.0200 | 0.0200 | 0.0200 | 0.0200 | 0.0200 | 0.0200 |
| Fe2O3(wt%)≤ | 0.0030 | 0.0050 | —— | —— | 0.0030 | 0.0030 | 0.0030 |
| TiO2(wt%)≤ | 0.0020 | 0.0020 | 0.0010 | 0.0020 | 0.0020 | 0.0020 | 0.0020 |
| Na2O(wt%)≤ | 0.0050 | —— | 0.0100 | 0.0200 | 0.0500 | 0.0500 | 0.0500 |
| lg.Loss(wt%)≤ | 1.0 | 5.0 | 1.0 | 5.0 | 1.0 | 1.0 | 1.0 |
| ρ粒(g/cm)3 | —— | 1.15-1.45 | —— | 1.15-1.45 | —— | —— | —— |
| BET(m2/g) | 6~9,11~15 | 6~9,11~15 | 11~15 | ≤15 | 6~9,11~15 | —— | —— |
| D50(μm)≤ | 1 | 1.4 | 1 | 1.4 | 1 | 1 | 1 |