表面光滑
抗热震性强
精细度高
耐腐蚀
拨打 185-7543-7000 
| ZrO₂+HfO₂ | >94% |
| SiO₂ | < 0.015% |
| Fe₂O₃ | < 0.002% |
| Na₂O | < 0.005% |
| TiO₂ | <0.002% |
| Y₂O₃ | 5.56% |
| D50 | 64.67 μm |
| 主要成分 | Composition | W t% | ZrO₂+Y₂O₃≥99.5% |
| 密度 | Specific Density | g/cm3 | >6.05 |
| 硬度 | Hardness(HV) | Gpa | >12.0 |
| 热膨胀系数 | Coefficient of thermal expansion | (10-6/K) | 9.6(20-400°C) |
| 抗弯强度 | Bending Strength | Mpa | >1150 |
| 弹性模量 | Elastic Modulus | Gpa | 205 |
| 晶粒大小 | Grain Size | μm | <0.5 |
| 热导率 | Thermal Conductivity | W/(m-k) | 2.5 |